stainless steel cutting blade segment dedicated

 Special stainless steel cutting blade Category:
1, the surface chromium nitride alloy plating
(Seven color), this cutting stainless steel and alloy coatings and materials when compared to the general coating abrasion Edge 2000 Pads  resistance, the resistance will be reduced under high-speed operation, in order to prolong the life of the blade and maintain long-term action under the stability. Adding cobalt and the blade, the saw blade can effectively improve the stability, hardness and wear resistance. The blade can reduce the cobalt content increases, the coefficient of friction between the workpiece. Its durability is the ordinary high-speed steel 1 to 2 times. This blade especially for stainless steel tubing, rods, profiles sawing, cutting, cutting, milling. Used in the processing of ordinary steel, aluminum, plastic, wood and other materials, the effect is very obvious, less burr after cutting section, blade toughness, cutting and long life. Machinable stainless steel tube material: 3-Series industrial stainless steel.
2, oxidation coating
: After the steam treatment, the blade, the wood band saw blades  surface oxide layer (Fe3O4), this blade surface smoothness, and help to enhance the self-lubricating ability of the blade, the blade material stuck phenomenon is to a certain extent can be avoided on the cooling ability to absorb better, but compared to other coated blade, cutting the number of relatively less, which is usually the most common one we saw. HSS film - oxide coating technology parameters:
Coating thickness: about 5-10 microns
Surface hardness: about 900HV
Friction coefficient: 0.65
Machinable stainless steel tube material: 3-Series industrial stainless steel.
3, titanium coating
: After special treatment, the blade PVD coating, the surface was gold, the surface hardness of 2400HV, compared to steam treatment saw increased nearly three-fold, Mocha coefficient decreased to 0.55 for the semi-automatic or fully automatic metal circular sawing machine Quick Sawing seamless, iron pipes, rods, etc., faster than the steam treatment saw doubling, effectively reducing the cost cutting while in sawing stainless steel pipe, it can get quite satisfactory cutting results. HSS piece - titanium coating technology parameters:
Coating thickness: about 5 microns
Surface hardness: about 2200-2400HV
Oxidation temperature: 600 ℃
Friction coefficient: 0.55
Machinable stainless steel tube material: 3-Series industrial stainless steel.
4, purplish blue coat
: The use of multi-layer PVD coating treated blade to achieve a very low coefficient of friction, suitable for floor polisher pads  high cutting speeds and high feed rate used under the fine processing, and can significantly reduce litter on the edge adhesion . For cutting hard metal material, a copper alloy cut, cutting titanium, and an adhesive material cutting phenomenon is particularly frequent. High surface hardness of the blade allows for high-speed cutting work with other than uncoated blades, feed can be increased by 100%, increase the service life of the saw blade. This blade makes cutting surface is very smooth, saw more wear, so the cutting speed should be increased by 100%. HSS film - purplish blue coating technology parameters:
Coating thickness: about 5 microns
Surface hardness: about 3000-3300HV
Oxidation temperature: 450 ℃
Friction coefficient: 0.25
Machinable stainless steel tube material: stainless steel 3-series and two series of industrial stainless steel decorative materials.